Boron-containing molecular sieve CHA

ABSTRACT

A boron-containing molecular sieve having the CHA crystal structure and comprising (1) silicon oxide and (2) boron oxide or a combination of boron oxide and aluminum oxide, iron oxide, titanium oxide, gallium oxide and mixtures thereof is prepared using a quaternary ammonium cation derived from 1-adamantamine, 3-quinuclidinol or 2-exo-aminonorbornane as structure directing agent. The molecular sieve can be used for gas separation or in catalysts to prepare methylamine or dimethylamine, to convert oxygenates (e.g., methanol) to light olefins, or for the reduction of oxides of nitrogen n a gas stream (e.g., automotive exhaust).

This application claims the benefit under 35 USC 119 of copendingProvisional Application No. 60/632022, filed Nov. 30, 2004.

BACKGROUND

Chabazite, which has the crystal structure designated “CHA”, is anatural zeolite with the approximate formula Ca₆Al₁₂Si₂₄O₇₂. Syntheticforms of chabazite are described in “Zeolite Molecular Sieves” by D. W.Breck, published in 1973 by John Wiley & Sons. The synthetic formsreported by Breck are: zeolite “K-G”, described in J. Chem. Soc., p.2822 (1956), Barrer et al.; zeolite D, described in British Patent No.868,846 (1961); and zeolite R, described in U.S. Pat. No. 3,030,181,issued Apr. 17, 1962 to Milton et al. Chabazite is also discussed in“Atlas of Zeolite Structure Types” (1978) by W. H. Meier and D. H.Olson.

The K-G zeolite material reported in the J. Chem. Soc. Article by Barreret al. is a potassium form having a silica:alumina mole ratio (referredto herein as “SAR”) of 2.3:1 to 4.15:1. Zeolite D reported in BritishPatent No. 868,846 is a sodium-potassium form having a SAR of 4.5:1 to4.9:1. Zeolite R reported in U.S. Pat. No. 3,030,181 is a sodium formwhich has a SAR of 3.45:1 to 3.65:1.

Citation No. 93:66052y in Volume 93 (1980) of Chemical Abstractsconcerns a Russian language article by Tsitsishrili et al. in Soobsch.Akad. Nauk. Gruz. SSR 1980, 97(3) 621-4. This article teaches that thepresence of tetramethylammonium ions in a reaction mixture containingK₂O—Na₂O—SiO₂—Al₂O₃—H₂O promotes the crystallization of chabazite. Thezeolite obtained by the crystallization procedure has a SAR of 4.23.

The molecular sieve designated SSZ-13, which has the CHA crystalstructure, is disclosed in U.S. Pat. No. 4,544,538, issued Oct. 1, 1985to Zones. SSZ-13 is prepared from nitrogen-containing cations derivedfrom 1-adamantamine, 3-quinuclidinol and 2-exo-aminonorbornane. Zonesdiscloses that the SSZ-13 of U.S. Pat. No. 4,544,538 has a composition,as-synthesized and in the anhydrous state, in terms of mole ratios ofoxides as follows:

(0.5 to 1.4)R₂O:(0 to 0.5)M₂O:W₂O₃:(greater than 5)YO₂ wherein M is analkali metal cation, W is selected from aluminum, gallium and mixturesthereof, Y is selected from silicon, germanium and mixtures thereof, andR is an organic cation. U.S. Pat. No. 4,544,538 does not, however,disclose boron-containing SSZ-13.

U.S. Pat. No. 6,709,644, issued Mar. 23, 2004 to Zones et al., discloseszeolites having the CHA crystal structure and having small crystallitesizes. It does not, however, disclose a CHA zeolite containing boron. Itis disclosed that the zeolite can be used for separation of gasses(e.g., separating carbon dioxide from natural gas), and in catalystsused for the reduction of oxides of nitrogen in a gas stream (e.g.,automotive exhaust), converting lower alcohols and other oxygenatedhydrocarbons to liquid products, and for producing dimethylamine.

SUMMARY OF THE INVENTION

In accordance with the present invention there is provided aboron-containing molecular sieve having the CHA crystal structure andcomprising (1) silicon oxide and (2) boron oxide or a combination ofboron oxide and aluminum oxide, iron oxide, titanium oxide, galliumoxide and mixtures thereof. Preferably, oxide (2) is more than 50% boronoxide on a molar basis.

In accordance with this invention there is provided a method forpreparing a boron-containing molecular sieve having the CHA crystalstructure and comprising (1) silicon oxide and (2) boron oxide or acombination of boron oxide and aluminum oxide, iron oxide, titaniumoxide, gallium oxide and mixtures thereof, said method comprising:

A. forming an aqueous reaction mixture comprising a composition in termsof mole ratios falling within the following ranges:

YO₂/W_(a)O_(b)    >2–2,000 OH—/YO₂ 0.2–0.45 Q/YO₂ 0.2–0.45 M_(2/n)O/YO₂  0–0.25 H₂O/YO₂ 22–80 wherein Y is silicon, W is boron or a combination of boron and aluminum,iron, titanium, gallium and mixtures thereof; a is 1 or 2 and b is 2when a is 1 (i.e., W is tetravalent) or b is 3 when a is 2 (i.e., W istrivalent); M is an alkali metal or alkaline earth metal, n is thevalence of M (i.e., 1 or 2), and Q is a quaternary ammonium cationderived from 1-adamantamine, 3-quinuclidinol or 2-exo-aminonorbornane;andB. maintaining said aqueous mixture under sufficient crystallizationconditions until crystals are formed.

In accordance with this invention, there is also provided aboron-containing molecular sieve having the CHA crystal structure andhaving a composition, as-synthesized and in the anhydrous state, interms of mole ratios of oxides as follows:

YO₂/W_(c)O_(d)  20–2,000 M_(2/n)O/YO₂  0–0.03 Q/YO₂ 0.02–0.05  wherein Y is silicon, W is boron or a combination of boron and aluminum,iron, titanium, gallium and mixtures thereof; c is 1 or 2; d is 2 when cis 1 (i.e., W is tetravalent) or d is 3 or 5 when c is 2 (i.e., d is 3when W is trivalent or 5 when W is pentavalent); M is an alkali metalcation, alkaline earth metal cation or mixtures thereof; n is thevalence of M (i.e., 1 or 2); and Q is a quaternary ammonium cationderived from 1-adamantamine, 3-quinuclidinol or 2-exo-aminonorbornane.

DETAILED DESCRIPTION

The present invention relates to molecular sieves having the CHA crystalstructure and containing boron in their crystal framework.

Boron-containing CHA molecular sieves can be suitably prepared from anaqueous reaction mixture containing sources of sources of an oxide ofsilicon; sources of boron oxide or a combination of boron oxide andaluminum oxide, iron oxide, titanium oxide, gallium oxide and mixturesthereof; optionally sources of an alkali metal or alkaline earth metaloxide; and a cation derived from 1-adamantamine, 3-quinuclidinol or2-exo-aminonorbornane. The mixture should have a composition in terms ofmole ratios falling within the ranges shown in Table A below:

TABLE A YO₂/W_(a)O_(b)    >2–2,000 OH—/YO₂ 0.2–0.45 Q/YO₂ 0.2–0.45M_(2/n)O/YO₂   0–0.25 H₂O/YO₂ 22–80 wherein Y is silicon; W is boron or a combination of boron and aluminum,iron, titanium, gallium and mixtures thereof; M is an alkali metal oralkaline earth metal; n is the valence of M (i.e., 1 or 2) and Q is aquaternary ammonium cation derived from 1-adamantamine, 3-quinuclidinolor 2-exo-aminonorbornane (commonly known as a structure directing agentor “SDA”).

The quaternary ammonium cation derived from 1-adamantamine can be aN,N,N-trialkyl-1-adamantammonium cation which has the formula:

where R¹, R², and R³ are each independently a lower alkyl, for examplemethyl. The cation is associated with an anion, A⁻, which is notdetrimental to the formation of the molecular sieve. Representative ofsuch anions include halogens, such as fluoride, chloride, bromide andiodide; hydroxide; acetate; sulfate and carboxylate. Hydroxide is thepreferred anion. It may be beneficial to ion exchange, for example, ahalide for hydroxide ion, thereby reducing or eliminating the alkalimetal or alkaline earth metal hydroxide required.

The cation derived from 3-quinuclidinol is a cation derived from:

The quaternary ammonium cation derived from 3-quinuclidinol can have theformula:

where R¹, R², R³ and A are as defined above.

The quaternary ammonium cation derived from 2-exo-aminonorbornane canhave the formula:

where R¹, R², R³ and A are as defined above.

The reaction mixture is prepared using standard molecular sievepreparation techniques. Typical sources of silicon oxide include fumedsilica, silicates, silica hydrogel, silicic acid, colloidal silica,tetra-alkyl orthosilicates, and silica hydroxides. Sources of boronoxide include borosilicate glasses and other reactive boron compounds.These include borates, boric acid and borate esters. Typical sources ofaluminum oxide include aluminates, alumina, hydrated aluminumhydroxides, and aluminum compounds such as AlCl₃ and Al₂(SO₄)₃. Sourcesof other oxides are analogous to those for silicon oxide, boron oxideand aluminum oxide.

It has been found that seeding the reaction mixture with CHA crystalsboth directs and accelerates the crystallization, as well as minimizingthe formation of undesired contaminants. In order to produce pure phaseboron-containing CHA crystals, seeding may be required. When seeds areused, they can be used in an amount that is about 2–3 weight percentbased on the weight of YO₂.

The reaction mixture is maintained at an elevated temperature until CHAcrystals are formed. The temperatures during the hydrothermalcrystallization step are typically maintained from about 120° C. toabout 160° C. It has been found that a temperature below 160° C., e.g.,about 120° C. to about 140° C., is useful for producing boron-containingCHA crystals without the formation of secondary crystal phases.

The crystallization period is typically greater than 1 day andpreferably from about 3 days to about 7 days. The hydrothermalcrystallization is conducted under pressure and usually in an autoclaveso that the reaction mixture is subject to autogenous pressure. Thereaction mixture can be stirred, such as by rotating the reactionvessel, during crystallization.

Once the boron-containing CHA crystals have formed, the solid product isseparated from the reaction mixture by standard mechanical separationtechniques such as filtration. The crystals are water-washed and thendried, e.g., at 90° C. to 150° C. for from 8 to 24 hours, to obtain theas-synthesized crystals. The drying step can be performed at atmosphericor subatmospheric pressures.

The boron-containing CHA molecular sieve has a composition,as-synthesized and in the anhydrous state, in terms of mole ratios ofoxides as indicated in Table B below:

As-Synthesized Boron-containing CHA Composition

TABLE B YO₂/W_(c)O_(d)  20–2,000 M_(2/n)O/YO₂  0–0.03 Q/YO₂ 0.02–0.05  where Y, W, M, n and Q are as defined above.

The boron-containing CHA molecular sieves, as-synthesized, have acrystalline structure whose X-ray powder diffraction (“XRD”) patternshows the following characteristic lines:

TABLE I As-Synthesized Boron-Containing CHA XRD 2 Theta^((a)) d-spacing(Angstroms) Relative Intensity^((b)) 9.68 9.13 S 14.17 6.25 M 16.41 5.40VS 17.94 4.94 M 21.13 4.20 VS 25.21 3.53 VS 26.61 3.35 W–M 31.11 2.87 M31.42 2.84 M 31.59 2.83 M ^((a))±0.10 ^((b))The X-ray patterns providedare based on a relative intensity scale in which the strongest line inthe X-ray pattern is assigned a value of 100: W(weak) is less than 20;M(medium) is between 20 and 40; S(strong) is between 40 and 60; VS(verystrong) is greater than 60.

Table IA below shows the X-ray powder diffraction lines foras-synthesized boron-containing CHA including actual relativeintensities.

TABLE IA As-Synthesized Boron-Containing CHA XRD 2 Theta^((a)) d-spacing(Angstroms) Relative Intensity (%) 9.68 9.13 55.2 13.21 6.70 5.4 14.176.25 33.5 16.41 5.40 81.3 17.94 4.94 32.6 19.43 4.56 6.8 21.13 4.20 10022.35 3.97 15.8 23.00 3.86 10.1 23.57 3.77 5.1 25.21 3.53 78.4 26.613.35 20.2 28.37 3.14 6.0 28.57 3.12 4.4 30.27 2.95 3.9 31.11 2.87 29.831.42 2.84 38.3 31.59 2.83 26.5 32.27 2.77 1.4 33.15 2.70 3.0 33.93 2.644.7 35.44 2.53 3.9 35.84 2.50 1.2 36.55 2.46 10.9 39.40 2.29 1.8 40.022.25 1.3 40.44 2.23 1.0 40.73 2.21 6.0 ^((a))±0.10

After calcination, the boron-containing CHA molecular sieves have acrystalline structure whose X-ray powder diffraction pattern include thecharacteristic lines shown in Table II:

TABLE II Calcined Boron-Containing CHA XRD 2 Theta^((a)) d-spacing(Angstroms) Relative Intensity 9.74 9.07 VS 13.12 6.74 M 14.47 6.12 W16.38 5.41 W 18.85 4.78 M 21.07 4.21 M 25.98 3.43 W 26.46 3.37 W 31.302.86 W 32.15 2.78 W ^((a))±0.10

Table IIA below shows the X-ray powder diffraction lines for calcinedboron-containing CHA including actual relative intensities.

TABLE IIA Calcined Boron-Containing CHA XRD 2 Theta^((a)) d-spacing(Angstroms) Relative Intensity (%) 9.74 9.07 100 13.12 6.74 29.5 14.476.12 4.6 16.38 5.41 14.2 18.85 4.78 22.1 19.60 4.53 2.2 21.07 4.21 32.922.84 3.89 2.2 23.68 3.75 0.8 25.98 3.43 13.1 26.46 3.37 8.7 28.27 3.151.3 29.24 3.05 1.6 30.32 2.95 1.7 31.30 2.86 14.4 32.15 2.78 9.0 32.562.75 0.2 35.26 2.54 2.4 ^((a))±0.10

The X-ray powder diffraction patterns were determined by standardtechniques. The radiation was the K-alpha/doublet of copper and ascintillation counter spectrometer with a strip-chart pen recorder wasused. The peak heights I and the positions, as a function of 2 Thetawhere Theta is the Bragg angle, were read from the spectrometer chart.From these measured values, the relative intensities, 100×I/Io, where Iois the intensity of the strongest line or peak, and d, the interplanarspacing in Angstroms corresponding to the recorded lines, can becalculated.

Variations in the diffraction pattern can result from variations in themole ratio of oxides from sample to sample. The molecular sieve producedby exchanging the metal or other cations present in the molecular sievewith various other cations yields a similar diffraction pattern,although there can be shifts in interplanar spacing as well asvariations in relative intensity. Calcination can also cause shifts inthe X-ray diffraction pattern. Also, the symmetry can change based onthe relative amounts of boron and aluminum in the crystal structure.Notwithstanding these perturbations, the basic crystal lattice structureremains unchanged.

Boron-containing CHA molecular sieves are useful in adsorption, incatalysts useful in converting methanol to olefins, synthesis of amines(such as dimethylamine), in the reduction of oxides of nitrogen ingasses (such as automobile exhaust), and in gas separation.

EXAMPLES Examples 1–14

Boron-containing CHA is synthesized by preparing the gel compositions,i.e., reaction mixtures, having the compositions, in terms of moleratios, shown in the table below. The resulting gel is placed in a Parrbomb reactor and heated in an oven at the temperature indicated belowwhile rotating at the speed indicated below. Products are analyzed byX-ray diffraction (XRD) and found to be boron-containing molecularsieves having the CHA structure. The source of silicon oxide is CabosilM-5 fumed silica or HiSil 233 amorphous silica (0.208 wt. % alumina).The source of boron oxide is boric acid and the source of aluminum oxideis Reheis F 2000 alumina.

Ex. # SiO₂/B₂O₃ SiO₂/Al₂O₃ H₂O/SiO₂ OH—/SiO₂ Na+/SiO₂ SDA/SiO₂ Rx Cond.¹Seeds %1-ada² 1 2.51 1,010 23.51 0.25 0.20 0.25 140/43/5 d yes 100 212.01 1,010 22.74 0.25 0.08 0.25 140/43/5 d yes 100 3 12.33 1,010 22.510.25 0.08 0.25 140/43/5 d yes 100 4 12.07 288,900 23.00 0.26 0.09 0.26140/43/5 d no 100 5 12.33 37,129 22.51 0.25 0.09 0.25 140/43/5 d yes 1006 12.33 248,388 22.51 0.25 0.09 0.25 140/43/5 d yes 100 7 12.33 248,38822.53 0.25 0.09 0.25 140/43/5 d yes 100 8 12.33 248,388 22.53 0.25 0.000.25 140/43/5 d yes 100 9 12.33 248,388 22.51 0.25 0.09 0.25 160/43/4 dyes 100 10 11.99 288,900 23.18 0.26 0.09 0.26 160/43/4 d no 100 11 12.13288,900 32.22 0.43 0.21 0.21 160/43/4 d no 100 12 11.99 288,900 23.160.26 0.00 0.26 160/43/4 d no 100 13 11.99 288,900 23.18 0.26 0.09 0.26160/43/4 d no 100 14 3.08 248,388 22.51 0.25 0.00 0.25 160/43/6 d yes100 ¹° C./RPM/Days ²1-ada = Quaternary ammonium cation derived from1-adamantamine

Examples 15–20 Deboronation

Boron is removed from samples of the molecular sieves prepared asdescribed in Example 13 above and then calcined. The sample is heated inan acid solution under the conditions indicated in the table below. Theresults are shown in the table.

Ex. No. Starting Deboronation Rx (B) SSZ-13 15 16 17 18 19 20 Acid used— Acetic acid acetic acid acetic acid HCl HCl HCl Acid Molarity — 1.0 M0.01 M 0.0001 M 0.01 M 0.001 M 0.0001 M Rx Cond. — 45 C./0 rpm/19 hr 45C./0 rpm/19 hr 45 C./0 rpm/19 hr 45 C./0 rpm/19 hr 45 C./0 rpm/19 hr 45C./0 rpm/19 hr Analysis Results Untreated Treated Treated TreatedTreated Treated Treated Boron 0.66% 614 ppm 513 ppm 420 ppm 421 ppm 506ppm 552 ppm XRD CHA CHA CHA CHA CHA CHA CHA

1. A method for preparing a boron-containing molecular sieve having theCHA crystal structure and comprising (1) silicon oxide and (2) boronoxide or a combination of boron oxide and aluminum oxide, iron oxide,titanium oxide, gallium oxide and mixtures thereof, said methodcomprising: A. forming an aqueous reaction mixture comprising acomposition in terms of mole ratios falling within the following ranges:YO₂/W_(a)O_(b)    >2–2,000 OH—/YO₂ 0.2–0.45 Q/YO₂ 0.2–0.45 M_(2/n)O/YO₂  0–0.25 H₂O/YO₂ 22–80 

 wherein Y is silicon, W is boron or a combination of boron and aluminumiron, titanium, gallium and mixtures thereof; a is 1 or 2 and b is 2when a is 1 or b is 3 when a is 2; M is an alkali metal or alkalineearth metal, n is the valence of M, Q is a quaternary ammonium cationdelved from 1-adamantamine, 3-quinuclidinol or 2-exo-aminonorbornane andwherein the aqueous reaction mixture does not contain fluorine; and B.maintaining said aqueous mixture under sufficient crystallizationconditions until crystals are formed.
 2. The method of claim 1 whereinoxide (2) is more than 50% boron oxide on a molar basis.
 3. The methodof claim 1 wherein Y is silicon and W is boron.
 4. A boron-containingmolecular sieve having the CHA crystal structure and having acomposition, as-synthesized and in the anhydrous state, in terms of moleratios of oxides as follows: YO₂/W_(c)O_(d)  20–2,000 M_(2/n)O/YO₂ 0–0.03 Q/YO₂ 0.02–0.05  

wherein Y is silicon, , W is boron or a combination of boron andaluminum, iron, titanium, gallium and mixtures thereof; c is 1 or 2; dis 2 when c is 1 or d is 3 or 5 when c is 2; M is an alkali metalcation, alkaline earth metal cation or mixtures thereof; n is thevalence of M (i.e., 1 or 2); Q is a quaternary ammonium cation derivedfrom 1-adamantamine, 3-quinuclidinol or 2-exo-aminonorbornane andwherein the as-synthesized molecular sieve does not contain fluorine. 5.The molecular sieve of claim 4 wherein oxide (2) is more than 50% boronoxide on a molar basis.
 6. The as-synthesized molecular sieve of claim 4wherein Y is silicon and W is boron.